SUOYI One-Stop Production Solution for Dental Zirconia Blocks
2026-05-25
SUOYI One-Stop Production Solution for Dental Zirconia Blocks
Raw Material Preparation → Pre-forming Treatment → Sintering Process → Post-processing
1. Core Production Process and Equipment
1.1 Raw Material Preparation: Dental Yttrium Stabilized Zirconia Powder + Mixer + Vibrating Screen
Using 3Y/4Y/5Y yttrium stabilized zirconia powder as the core raw material, the components are uniformly mixed using a mixer, and then sieved using a vibrating screen to remove impurities, ensuring uniform particle size and satisfactory flowability. The recommended configuration for the vibrating screen in this solution is a 6-layer linear vibrating screen with a sieving capacity of over 95%.
Using 3Y/4Y/5Y yttrium stabilized zirconia powder as the core raw material, the components are uniformly mixed using a mixer, and then sieved using a vibrating screen to remove impurities, ensuring uniform particle size and satisfactory flowability. The recommended configuration for the vibrating screen in this solution is a 6-layer linear vibrating screen with a sieving capacity of over 95%.
1.2 Pre-forming: Dry Press + Vacuum Press
The zirconia block blanks are initially pressed using a dry press, and a vacuum press removes air bubbles from the blanks, improving density.
The zirconia block blanks are initially pressed using a dry press, and a vacuum press removes air bubbles from the blanks, improving density.
1.3 Dense Forming: Cold Isostatic Press
The pre-pressed blanks are uniformly pressurized to further improve density uniformity and reduce deformation during subsequent sintering.
The pre-pressed blanks are uniformly pressurized to further improve density uniformity and reduce deformation during subsequent sintering.
1.4 Sintering and Densification: Vacuum Pressure Atmosphere Sintering Furnace/Vacuum Hot Press Sintering Furnace
The cold isostatically pressed blank is fed into the sintering furnace and sintered at 1300-1600℃ in a vacuum environment to obtain a dense zirconium block matrix. The vacuum pressure atmosphere sintering furnace is specifically designed for zirconium oxide ceramics, providing a stable sintering environment free from impurities and oxidation. The vacuum hot press sintering furnace allows for simultaneous heating and pressurization, suitable for the preparation of high-performance, special-specification zirconium blocks.
The cold isostatically pressed blank is fed into the sintering furnace and sintered at 1300-1600℃ in a vacuum environment to obtain a dense zirconium block matrix. The vacuum pressure atmosphere sintering furnace is specifically designed for zirconium oxide ceramics, providing a stable sintering environment free from impurities and oxidation. The vacuum hot press sintering furnace allows for simultaneous heating and pressurization, suitable for the preparation of high-performance, special-specification zirconium blocks.
1.5 Finished Product Machining: CNC Engraving Machine/3D Printer
The sintered zirconium blocks are then machined to obtain finished zirconium blocks with uniform specifications. 3D printers can directly produce personalized, customized dental restoration parts, offering lower costs and higher efficiency compared to traditional CNC machining.
The sintered zirconium blocks are then machined to obtain finished zirconium blocks with uniform specifications. 3D printers can directly produce personalized, customized dental restoration parts, offering lower costs and higher efficiency compared to traditional CNC machining.
2. Extended Product Range
In addition to producing its core dental zirconium oxide blocks, SUOYI also manufactures compatible glass-ceramic blocks, PMMA (dental resin blocks), and other dental restoration materials to meet diverse clinical needs.
In addition to producing its core dental zirconium oxide blocks, SUOYI also manufactures compatible glass-ceramic blocks, PMMA (dental resin blocks), and other dental restoration materials to meet diverse clinical needs.
3. Zirconia blocks can be further categorized by yttrium oxide content:
3Y Zirconia: High strength, mostly used for posterior crowns and bridges.
4Y Zirconia: Balanced strength and translucency, suitable for anterior crowns and bridges.
5Y Zirconia: Optimal translucency, mostly used for anterior single crowns and veneers.
SUOYI Customized 4.5Y Yttrium Stabilized Zirconia Powder (YSZ) for Oxygen Sensors
SUOYI Invites You to the 30th China International Dental Equipment and Materials Exhibition 2026
Related Article
Nano titanium dioxide, also known as nano-titanium oxide, is an ultrafine functional titanium dioxide powder with a particle size controlled between 5–100 nm. It mainly consists of two commercially available crystalline phases: anatase and rutile. Unlike ordinary micron-sized titanium dioxide, the nanoscale structure brings unique photocatalytic effects, broad-spectrum ultraviolet blocking, high specific surface area, and superhydrophilicity,
SUOYI Multifunctional Inorganic New Material – Nano Titanium Dioxide (Nano TiO₂) Powder
Silicon oxide powder (SiO₂ powder) is a high-performance inorganic non-metallic powder material with excellent thermal stability, chemical resistance, electrical insulation properties, and low thermal expansion characteristics.
Due to its outstanding physical and chemical properties, silicon oxide powder has become an essential raw material in advanced ceramics, semiconductor packaging, electronic materials, energy storage, optical materials, and high-temperature applications.
Due to its outstanding physical and chemical properties, silicon oxide powder has become an essential raw material in advanced ceramics, semiconductor packaging, electronic materials, energy storage, optical materials, and high-temperature applications.
Suoyi Silica Powder – A Crucial Basic Powder for High-Performance Inorganic Materials
SUOYI Aluminum Nitride Powder: A Core Powder Material for High Thermal Conductivity and Insulation in the Electronic Semiconductor Industry
With the comprehensive iteration of third-generation semiconductors, AI computing chips, new energy power modules, and 5G RF devices, the miniaturization, high power, and high frequency of these devices bring the dual challenges of intense heat generation and high-voltage insulation.
With the comprehensive iteration of third-generation semiconductors, AI computing chips, new energy power modules, and 5G RF devices, the miniaturization, high power, and high frequency of these devices bring the dual challenges of intense heat generation and high-voltage insulation.
SUOYI Aluminum Nitride Powder: A Core Powder Material for High Thermal Conductivity and Insulation in the Electronic Semiconductor Industry