Melting point:2700℃
Boiling point:4300 ℃
Density:6.03g/cm3
Grade Standard:Electron Grade
Grade Standard:Industrial Grade
Grade Standard:Medicine Grade
Grade Standard:Reagent Grade
Classification:zirconium oxide
Appearance:White powder
Application:Ceramic
Place of Origin:CN
Brand Name:SuoYi
Purity:95%
Other Names:Zirconia
EINECS No.:215-222-5
MF:ZrO2
CAS No.:13463-67-7

High precision Yttria stabilized zirconia grinding balls/beads

1. High cost-effective, low wear and long lifetime

2. High specific gravity, high efficiency

3. Highly wear resistant to acid and solvents

4. Highly polished, smooth, easy to clean, low abrasion to the equipment

5. High mechanical strength, good toughness, impact resistance, no broken beads

Comosition	Wt%	94.8+-0.2% ZrO2 5.2+-0.2 Y2O3
Density	g/cm3	≥6.0
Hardness	Gpa	>12
Crushing Load	KN	≥25(S 6.5MM)
Fracture Toughness	Mpa.m1/2	>9
Grain Size	um	≤0.5
Modulus Of Elasticity	Gpa	200
Thermal Conductivity	W/(m.k)	3(20-400C)
Coefficent of thermal expansion	10-6 k-1	9.6(20-400C)

Available Size
1).0.1-0.2mm 0.2-0.3mm 0.3-0.4mm 0.4-0.6mm 0.6-0.8mm 0.8-1.0mm
2).1.0-1.2mm 1.2-1.4mm 1.4-1.6mm 1.6-1.8mm 1.8-2.0mm
3).2.0-2.2mm 2.2-2.4mm 2.4-2.6mm 2.6-2.8mm 2.8-3.2mm
4).3.0-3.5mm 3.5-4.0mm 4.0-4.5mm 4.5-5.0mm 5.0-5.5mm
5).5.5-6.0mm 6.0-6.5mm 6.5-7.0mm 8mm 10mm 15mm 20mm 25mm 30mm 50mm

Electronics Industry: Piezoelectric ceramic, inductance materials , inductance materials, capacitors ceramics semiconductor ceramic etc.
Battery Industry: lithium iron phosphate, cobalt acid lithium materials etc.
Chemical Industry: Paint materials, printing ink, paint etc.
Ceramic industry: Refractory materials , glaze materials, silica acid zirconia structure ceramics etc
Other: Food, medicine, cosmetics etc